Alkaline battery

ABSTRACT

An alkaline battery of this invention includes: a negative electrode including a negative electrode mixture that contains a zinc alloy as an active material, the zinc alloy containing at least aluminum; an alkaline electrolyte; and a positive electrode. The alkaline electrolyte includes an aqueous KOH solution and LiOH and an aluminum compound that are dissolved in the aqueous KOH solution. The alkaline battery has excellent high-rate discharge characteristics.

TECHNICAL FIELD

The present invention relates to alkaline batteries such as alkaline dry batteries and air batteries, and, more particularly, to an improvement in the alkaline electrolyte to prevent gas production and improve high-rate discharge characteristics.

BACKGROUND ART

A conventional problem with alkaline batteries using zinc or a zinc alloy as a negative electrode active material is that the active material corrodes in an alkaline electrolyte to produce hydrogen gas. Accumulation of this gas in the battery increases the battery inner pressure, thereby causing the electrolyte to leak out, which is disadvantageous.

To solve this problem, various techniques have been examined. Patent Document 1 discloses that adding lithium hydroxide to an electrolyte decreases the reactivity of the electrolyte with the surface of an active material powder, thereby reducing the amount of gas produced.

Patent Document 1: Japanese Laid-Open Patent

Publication No. Hei 2000-82503

DISCLOSURE OF INVENTION

Problem that the Invention is to Solve

However, in the case of a zinc alloy containing at least aluminum, even if LiOH is added to an alkaline electrolyte, a large amount of aluminum is dissolved in the electrolyte. Thus, there is a problem in that the addition of LiOH does not produce the effect of suppressing gas production from zinc, thereby resulting in degradation of high-rate discharge characteristics of the battery. The reason why the addition of LiOH suppresses gas production is probably that Zn(OH)₄ ²⁻ produced during discharge is prevented from changing into a passivation film on the active material surface and that a conductive film comprising Zn, O, and K is formed. However, in the case of using an aluminum-containing zinc alloy as a negative electrode active material, part of this conductive film is destroyed when the aluminum in the alloy is dissolved in an electrolyte. Hence, the zinc alloy is exposed at the surface, so that gas production cannot be sufficiently suppressed. As a result, a passivation film is formed to increase the resistance, thereby leading to a significant degradation of discharge characteristics, particularly high-rate discharge characteristics.

Means for Solving the Problem

In order to solve the above-mentioned problems, the present invention is directed to an alkaline battery including: a negative electrode including a negative electrode mixture that contains a zinc alloy as an active material, the zinc alloy containing at least aluminum; an alkaline electrolyte; and a positive electrode. The alkaline electrolyte includes an aqueous KOH solution and LiOH and an aluminum compound that are dissolved in the aqueous KOH solution.

According to this configuration, the aluminum in the negative electrode active material can be prevented from dissolving into the electrolyte, and the LiOH in the electrolyte can produce the effect of preventing Zn(OH)₄ ²⁻produced during discharge from depositing onto the active material surface as ZnO. That is, the LiOH added to the electrolyte suppresses formation of a passivation film (ZnO) on the zinc alloy surface during discharge, so that a conductive film comprising Zn, O, and K is formed. Also, the aluminum compound suppresses dissolution of the aluminum in the zinc alloy into the electrolyte. Accordingly, it is possible to improve the discharge characteristics, particularly high-rate discharge characteristics, of the battery.

If the amounts of LiOH and aluminum compound in the negative electrode mixture are less than 0.1 wt % and less than 0.001 wt %, respectively, relative to the whole amount of the negative electrode mixture, the dissolution of aluminum from the zinc alloy is not suppressed, and the addition of LiOH is not effective. Also, if the amounts of LiOH and aluminum compound are more than 2 wt % and 0.2 wt %, respectively, relative to the whole amount of the negative electrode mixture, it is difficult to maintain the pH of the electrolyte at a constant level among lots due to the influence of carbon dioxide, etc., depending on the management condition.

Therefore, in order to ensure the effects obtained by the addition of LiOH and the aluminum compound and improve the discharge characteristics, particularly high-rate discharge characteristics, of the battery, it is preferred that the amounts of LiOH and aluminum compound contained in the electrolyte in the negative electrode mixture be in the range of 0.1 to 2 wt % and in the range of 0.001 to 0.2 wt %, respectively, relative to the whole negative electrode mixture. As used therein, the negative electrode mixture refers to a mixture of the active material zinc alloy and the electrolyte, and if the electrolyte is gelled, the negative electrode mixture contains a gelling agent.

Further, if the weight ratio of the whole electrolyte (i.e., the electrolyte contained in the entire battery, not the electrolyte contained in the negative electrode mixture) to the weight of the active material zinc alloy is less than 0.1, the concentration of Zn(OH)₄ ²⁻ around the zinc alloy sharply increases, so that the addition is not effective and the high-rate discharge characteristics of the battery deteriorates. Also, if this weight ratio is greater than 2, the ratio of the electrolyte to the negative electrode mixture increases excessively, so that the amount of active material powder in the negative electrode mixture decreases, thereby resulting in a decrease in battery capacity. It is therefore preferred that the weight ratio of the whole alkaline electrolyte to the zinc alloy of the negative electrode mixture be in the range of 0.1 to 2.

With respect to the composition of the zinc alloy, if an element selected from the group consisting of bismuth, indium, calcium, tin, and lead, which have high hydrogen overvoltages, is contained in addition to aluminum, the effect of suppressing gas production increases.

Also, exemplary aluminum compounds added include those soluble in the alkaline aqueous solution, such as Al(OH)₃ and aluminate. They are believed to exist in the electrolyte as aluminate ions (Al(OH)₄(H₂O)₂ ⁻, Al(OH)₆(H₂O)³⁻, etc).

EFFECTS OF THE INVENTION

The present invention can optimize the relation between the zinc alloy and the electrolyte and improve both electrolyte-leakage resistance and high-rate discharge characteristics of the battery.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a partially sectional front view of an alkaline dry battery according to Embodiment 1 of the present invention; and

FIG. 2 is a partially sectional front view of an air battery according to Embodiment 2 of the present invention.

BEST MODE FOR CARRYING OUT THE INVENTION

Embodiments of the present invention are hereinafter described with reference to drawings.

Embodiment 1

The structure of an alkaline dry battery is described with reference to FIG. 1, which is a partially sectional front view.

A battery case 1 contains a positive electrode mixture 2 in the form of short cylindrical pellets, a separator 4, and a gelled negative electrode mixture 3. The battery case 1 may be a steel case whose inner face is plated with nickel. A plurality of the positive electrode mixture pellets 2 are contained in the battery case 1 so as to closely adhere to the inner face thereof. The separator 4 is placed on the inner side of the positive electrode mixture 2, and the gelled negative electrode mixture 3 is filled in the space on the inner side of the separator 4.

The positive electrode mixture 2 is prepared as follows. First, manganese dioxide, graphite, and an electrolyte are mixed together in a weight ratio of 90:6:1. The resultant mixture is sufficiently stirred and then compression molded into flakes. Subsequently, the positive electrode mixture flakes are crushed to obtain positive electrode mixture granules, and the positive electrode mixture granules are then classified with a sieve to obtain granules of 10 to 100 mesh. The resultant granules are compression molded into hollow cylinders to obtain the positive electrode mixture pellets 2. Four positive electrode mixture pellets 2 are inserted into the battery case 1, and the positive electrode mixture 2 is again molded by means of a compressing device so as to closely adhere to the inner wall of the battery case 1.

The separator 4, which is a cylinder with a bottom, is placed in the middle of the positive electrode mixture 2 that is placed in the battery case 1 in the above manner, and a predetermined amount of an alkaline electrolyte is injected into the space on the inner side of the separator 4. After the lapse of a predetermined time, the gelled negative electrode mixture 3, which comprises the alkaline electrolyte, a gelling agent, and a zinc alloy powder, is filled into the space on the inner side of the separator 4. The gelled negative electrode mixture 3 used is composed of 1 part by weight of sodium polyacrylate serving as the gelling agent, 33 parts by weight of the alkaline electrolyte, and 66 parts by weight of the zinc alloy powder. Also, the separator 4 used is a 220-μm-thick non-woven fabric composed of polyvinyl alcohol fibers and rayon fibers in a weight ratio of 7:10. The density of the separator is 0.30 g/cm³, and the size of the separator fibers is 0.3 denier. The ratio of the fibers is not limited to this, and other fibers may be added as a binder.

Subsequently, a negative electrode current collector 6 is inserted into the middle of the gelled negative electrode mixture 3. The negative electrode current collector 6 is integrally combined with a gasket 5 and a bottom plate 7 serving as the negative electrode terminal. The open edge of the battery case 1 is crimped onto the circumference of the bottom plate 7 with the edge of the gasket 5 interposed therebetween, to seal the opening of the battery case 1. Lastly, the outer face of the battery case 1 is covered with an outer label 8.

The electrolyte used is an alkaline electrolyte prepared by dissolving KOH in water. The KOH concentration of the alkaline electrolyte is 30 wt % to 45 wt %. In order to suppress the self-discharge of zinc, ZnO may be dissolved in the electrolyte, and with respect to the dissolution amount, ZnO may be dissolved until it becomes saturated at each alkali concentration. To reduce the production of hydrogen gas, an organic anti-corrosive agent may be dispersed in the electrolyte. The LiOH and aluminum compound contained in the negative electrode mixture are preferably added to the electrolyte at concentrations of 0.34 to 7.0 wt % and 0.0034 to 0.070 wt %, respectively.

Any organic anti-corrosive agent may be used as long as it suppresses the production of hydrogen, and an example is fluoroalkyl polyoxyethylene (trade name: Surflon #S-161). Also, the electrolyte may be in the state of gel. Any gelling agent may be used if it combines with the alkaline electrolyte to form gel, and examples other than sodium polyacrylate include carboxymethyl cellulose, polyvinyl alcohol, polyethylene oxide, polyacrylic acid, sodium polyacrylate, chitosan gel, and modified materials thereof obtained by changing the polymerization reaction, cross-linking degree, or molecular weight.

With respect to the form of the zinc alloy, for example, powder, a porous material obtained by sintering the powder, or a plate is effective. A zinc alloy powder can be obtained by synthesis from predetermined amounts of constituent elements by atomization and classification of the synthesized alloy. In addition to Zn, the zinc alloy contains Al, or contains Al and at least one element selected from the group consisting of Bi, In, Ca, Sn, and Pb. The suitable contents of other elements than Zn in the zinc alloy are 20 to 5000 ppm.

A porous zinc alloy obtained by sintering a zinc alloy powder is prepared by molding or hot-pressing a zinc alloy powder into pellets and sintering them in a reducing atmosphere in the range of 350 to 500° C.

A zinc alloy plate is prepared by forming lumps of a zinc alloy into a plate by using a roll press or the like. The thickness of this plate is arbitrarily adjusted so as to conform to the battery case. The plate surface may be flat, irregular due to punching, or perforated with through-holes.

Embodiment 2

The structure of an air battery is described with reference to FIG. 2. FIG. 2 is a partially sectional front view of an air battery. FIG. 2 illustrates the structure immediately after the fabrication; due to discharge, zinc in the negative electrode changes to a zinc oxide and undergoes a volume expansion, so that the space in an air diffusion chamber 16 changes to a size that is so large as to accommodate only an air diffusion paper 15.

A case serving as the positive electrode terminal is represented by numeral 11 and contains a separator 12, an air electrode 13 and a water-repellent film 14 on the bottom. Under them is the air diffusion chamber 16 for accommodating the air diffusion paper 15. The water-repellent film 14 allows oxygen to be supplied to the air electrode 13 and prevents an electrolyte from leaking out of the battery. The air diffusion paper 15 permits uniform diffusion of air that is introduced from an air vent 17 in the bottom of the case 11 into the case.

A sealing plate 18 serving as the negative electrode terminal contains a negative electrode mixture 19 comprising a zinc alloy powder and an electrolyte, and a ring-shaped insulating gasket 20 is fitted to the periphery thereof. The sealing plate is combined with the case 11, and the edge of the case 11 is crimped onto the sealing plate with the insulating gasket 20 therebetween, to seal the power generating element. Seal paper 21 affixed to the outer bottom face of the case closes the air vent 17 when the battery is not used, thereby blocking the entrance of air and preventing battery deterioration due to self-discharge. The air electrode 13 is produced by bonding a catalyst composition mainly composed of a metal oxide such as manganese dioxide, graphite, activated carbon, and a fluorocarbon binder to a current collector net under pressure.

EXAMPLES

Examples of the present invention are hereinafter described.

Example 1

AA-type alkaline dry batteries and coin-type PR2330 air batteries as described in Embodiments 1 and 2 were fabricated and evaluated for their characteristics.

As shown in Table 1, the zinc alloys of these negative electrodes are alloys containing Al or containing Al and one or more elements selected from the group consisting of Bi, In, Ca, Sn, and Pb, and there are three forms: powder, porous sintered material, and plate. Also, as shown in Table 2, the electrolytes used were 34 wt % aqueous KOH solutions to which LiOH and Al(OH)₃ were added in various ratios. These electrolytes contain 1.5 wt % of ZnO dissolved therein. The contents of Al and other elements in the negative electrode zinc alloy are as follows.

Al; 5 to 70 ppm, Bi; 50 to 400 ppm, In; 100 to 800 ppm, Ca; 2 to 50 ppm, Sn; 10 to 400 ppm, Pb; 2 to 50 ppm.

TABLE 1 Material Element added to zinc Zinc form A1 Al Powder A2 Al and Bi Powder A3 Al and In Powder A4 Al and Ca Powder A5 Al and Sn Powder A6 Al and Pb Powder A7 Al, Bi and In Powder A8 Al, In and Ca Powder A9 Al, Sn and Pb Powder A10 Al, Bi, In and Ca Powder A11 Al, Bi, In and Sn Powder A12 Al, Bi, In and Pb Powder A13 Al, Bi, In, Ca and Sn Powder A14 Al, Bi, In, Ca, Sn and Pb Powder B1 Al Porous sintered material B2 Al and Bi Porous sintered material B3 Al and In Porous sintered material B4 Al and Ca Porous sintered material B5 Al and Sn Porous sintered material B6 Al and Pb Porous sintered material B7 Al, Bi and In Porous sintered material B8 Al, In and Ca Porous sintered material B9 Al, Sn and Pb Porous sintered material B10 Al, Bi, In and Ca Porous sintered material B11 Al, Bi, In and Sn Porous sintered material B12 Al, Bi, In and Pb Porous sintered material B13 Al, Bi, In, Ca and Sn Porous sintered material B14 Al, Bi, In, Ca, Sn and Pb Porous sintered material C1 Al Plate C2 Al and Bi Plate C3 Al and In Plate C4 Al and Ca Plate C5 Al and Sn Plate C6 Al and Pb Plate C7 Al, Bi and In Plate C8 Al, In and Ca Plate C9 Al, Sn and Pb Plate C10 Al, Bi, In and Ca Plate C11 Al, Bi, In and Sn Plate C12 Al, Bi, In and Pb Plate C13 Al, Bi, In, Ca and Sn Plate C14 Al, Bi, In, Ca, Sn and Pb Plate

The respective batteries were placed in a constant temperature oven at 20° C. and a relative humidity of 60%. The air batteries were discharged at a current of 160 mA, and the alkaline dry batteries were discharged at a current of 1 A, whereby the discharge capacity C1 (mAh) was obtained. Also, the theoretical capacity C2 (mAh) was calculated from the weight of Zn contained in the negative electrode of each battery. The proportion P (%) of the discharge capacity Cl to the theoretical capacity C2 was calculated from the following formula (1), to evaluate the high-rate discharge characteristics of each battery. The higher P value a battery has, the better high-rate discharge characteristics the battery has. Also, to obtain battery capacity, the air batteries were discharged at a current of 3 mA and the alkaline dry batteries were discharged at a current of 50 mA. Table 2 shows the results. In the following Table 2 and Table 3, the wt % of LiOH and Al(OH)₃ represents the ratio relative to the negative electrode mixture.

P(%)=(C1/C2)×100   (1)

TABLE 2 Air battery Alkaline dry battery Electrolyte additive Discharge Discharge LiOH Al (OH)₃ capacity capacity Material (wt %) (wt %) P (%) (mAh) P (%) (mAh) A1 0 0 45 855 46 2223 A2 0.01 0.0001 62 865 63 2249 A3 0.05 0.0005 64 875 65 2275 A4 0.08 0.0008 65 899 66 2337 A5 0.1 0.001 91 920 93 2392 A6 0.2 0.005 93 925 95 2405 A7 0.8 0.01 91 922 93 2397 A8 1 0.05 92 919 94 2389 A9 1.3 0.1 89 930 91 2418 A10 1.5 0.15 88 925 90 2405 A11 1.8 0.18 87 915 89 2379 A12 2 0.2 86 905 88 2353 A13 2.5 0.25 66 878 67 2283 A14 3 0.3 62 869 63 2259 B1 0 0 46 860 47 2236 B2 0.01 0.0001 63 870 64 2262 B3 0.05 0.0005 65 880 66 2288 B4 0.08 0.0008 66 904 67 2350 B5 0.1 0.001 92 925 94 2405 B6 0.5 0.005 94 930 96 2418 B7 0.8 0.01 92 927 94 2410 B8 1 0.05 93 924 95 2402 B9 1.3 0.1 90 935 92 2431 B10 1.5 0.15 89 930 91 2418 B11 1.8 0.18 88 920 90 2392 B12 2 0.2 87 910 89 2366 B13 2.5 0.25 67 883 68 2296 B14 3 0.3 63 874 64 2272 C1 0 0 48 868 49 2257 C2 0.01 0.0001 65 878 66 2283 C3 0.05 0.0005 67 888 68 2309 C4 0.08 0.0008 68 912 69 2371 C5 0.1 0.001 94 933 95 2426 C6 0.5 0.005 96 938 97 2439 C7 0.8 0.01 94 935 95 2431 C8 1 0.05 95 932 96 2423 C9 1.3 0.1 92 943 94 2452 C10 1.5 0.15 91 938 93 2439 C11 1.8 0.18 90 928 92 2413 C12 2 0.2 89 918 91 2387 C13 2.5 0.25 69 891 70 2317 C14 3 0.3 65 882 66 2293

As is clear from Table 2, when LiOH and the aluminum compound are not added to the electrolyte, the P values of the air batteries are as low as 50% or less and the P values (%) of the alkaline dry batteries are also as low as 50% or less, in comparison with those when they are added. Although not shown in Table 2, when the electrolyte contains no aluminum compound and contains only LiOH, the aluminum in the zinc alloy dissolves in the electrolyte, thereby breaking the conductive film comprising Zn, O, and K. Also, when the electrolyte contains no LiOH and contains only the aluminum compound, a passivation film is formed on the zinc alloy surface. For these reasons, the P values (%) of both air batteries and alkaline dry batteries are as low as 50% or less.

As is clear from the above, in air batteries and alkaline dry batteries including as an active material a zinc alloy that contains at least aluminum, an alkaline electrolyte, and a positive electrode, the addition of LiOH and an aluminum compound to the alkaline electrolyte provides high discharge capacity on a high-rate discharge.

With respect to the amounts of LiOH and aluminum compound added, when the contents of LiOH and aluminum compound in the negative electrode mixture are lower than 0.1 wt % and 0.001 wt %, respectively, or higher than 2 wt % and 0.2 wt %, respectively, the P values (%) are in the 60% range. However, when the contents of LIOH and aluminum compound are 0.1 to 2 wt % and 0.001 to 0.2 wt %, respectively, the P values (%) are high, specifically 85% or more, which means that the high-rate discharge characteristics are excellent. Further, when the contents of LiOH and aluminum compound are 0.1 to 1 wt % and 0.001 to 0.05 wt %, respectively, the P values are high, specifically 92% or more, which means that the high-rate discharge characteristics are more preferable.

Note that the LiOH contents of 0.1 to 2 wt % in the negative electrode mixture correspond to 0.15 to 3 parts by weight per 100 parts by weight of the zinc alloy. Also, the aluminum compound contents of 0.001 to 0.2 wt % in the negative electrode mixture correspond to 0.0015 to 0.3 parts by weight per 100 parts by weight of the zinc alloy.

Also, if the amount of each element of Al, Bi, In, Ca, Sn, and Pb added to the zinc alloy used in the negative electrode is in the range of 20 ppm to 5000 ppm, gas production can be effectively prevented. If it is in the range of 50 ppm to 1000 ppm, gas production can be more effectively prevented.

Example 2

Next, using the alloy containing Al, Bi, and In in the negative electrode, air batteries and alkaline dry batteries were fabricated in the same manner as the above. Table 3 shows the electrolyte additives and the weight ratios of the electrolyte to the zinc alloy. It should be noted that in Example 1 the weight ratio of the electrolyte to the zinc alloy is 0.5.

These batteries were placed in a constant temperature oven at 20° C. and a relative humidity of 60%. The air batteries were discharged at a current of 165 mA, and the alkaline dry batteries were discharged at a current of 1050 mA, whereby the discharge capacity C1 was obtained. In the same manner as the above, the theoretical capacity C2 was calculated from the weight of Zn contained in the negative electrode of each battery, and the proportion P (%) of the discharge capacity C1 to the theoretical capacity C2 was calculated. Also, to obtain battery capacity, the air batteries were discharged at a current of 2 mA and the alkaline dry batteries were discharged at a current of 45 mA. Table 3 shows the results.

TABLE 3 Air battery Alkaline dry battery Electrolyte additive Electrolyte/ Discharge Discharge LiOH Al (OH)₃ zinc alloy capacity capacity Material (wt %) (wt %) (weight ratio) P (%) (mAh) P (%) (mAh) A7 0.21 0.001 0.05 82 921 84 2579 A7 0.21 0.001 0.08 85 923 87 2584 A7 0.21 0.001 0.1 90 925 92 2590 A7 0.21 0.001 0.8 91 925 93 2590 A7 0.21 0.001 1.5 92 920 94 2576 A7 0.21 0.001 2 93 910 95 2548 A7 0.21 0.001 2.5 94 720 96 2016 A7 0.21 0.001 3 94 500 96 1400 B7 0.21 0.001 0.05 83 926 85 2592 B7 0.21 0.001 0.08 86 928 88 2597 B7 0.21 0.001 0.1 91 930 93 2603 B7 0.21 0.001 0.8 92 930 94 2603 B7 0.21 0.001 1.5 93 925 95 2589 B7 0.21 0.001 2 94 915 96 2561 B7 0.21 0.001 2.5 95 724 97 2026 B7 0.21 0.001 3 95 503 97 1407 C7 0.21 0.001 0.05 85 933 86 2612 C7 0.21 0.001 0.08 88 935 89 2618 C7 0.21 0.001 0.1 93 937 94 2624 C7 0.21 0.001 0.8 94 937 95 2624 C7 0.21 0.001 1.5 95 932 96 2610 C7 0.21 0.001 2 96 922 97 2581 C7 0.21 0.001 2.5 97 729 98 2042 C7 0.21 0.001 3 97 507 98 1418

As is clear from Table 3, when the weight ratio of the whole electrolyte to the zinc alloy is less than 0.1, the P values (%) of the air batteries and the alkaline dry batteries were in the 80% range, and when the weight ratio of the whole electrolyte to the zinc alloy is greater than 2, the discharge capacities of the air batteries and the alkaline dry batteries at the discharge currents of 2 mA and 45 mA, respectively, were not more than 750 mAh and not more than 2100 mAh, respectively.

This shows that when the weight ratio of the whole electrolyte to the zinc alloy is in the range of 0.1 to 2, the P values (%) of the air batteries and the alkaline dry batteries are good, specifically 90% or higher, and that the discharge capacities of the air batteries and the alkaline dry batteries at the discharge currents of 2 mA and 45 mA, respectively, are good, specifically not less than 900 mAh and not less than 2500 mAh, respectively. Further, when the weight ratio of the whole electrolyte to the zinc alloy is in the range of 0.1 to 0.8, batteries having higher capacity can be obtained.

Also, if the amount of each element of Al, Bi, In, Ca, Sn, and Pb added to the zinc alloy used in the negative electrode is in the range of 20 ppm to 5000 ppm, gas production can be effectively prevented. If it is in the range of 50 ppm to 1000 ppm, gas production can be more effectively prevented.

INDUSTRIAL APPLICABILITY

The present invention is applied to alkaline batteries, such as air batteries and alkaline dry batteries, that use an aluminum-containing zinc alloy as a negative electrode active material. 

1. An alkaline battery comprising: a negative electrode including a negative electrode mixture that contains a zinc alloy as an active material, said zinc alloy containing at least aluminum; an alkaline electrolyte; and a positive electrode, wherein said alkaline electrolyte comprises an aqueous KOH solution and LiOH and an aluminum compound that are dissolved in said aqueous KOH solution.
 2. The alkaline battery in accordance with claim 1, wherein the amounts of the LiOH and the aluminum compound contained in the electrolyte in said negative electrode mixture are 0.1 to 2 wt % and 0.001 to 0.2 wt % of the negative electrode mixture, respectively.
 3. The alkaline battery in accordance with claim 1, wherein the amounts of the LiOH and the aluminum compound contained in the electrolyte in said negative electrode mixture are 0.15 to 3 parts by weight and 0.0015 to 0.3 parts by weight per 100 parts by weight of said zinc alloy.
 4. The alkaline battery in accordance with claim 1 or 2, wherein the weight ratio of the whole alkaline electrolyte to the zinc alloy of the negative electrode is 0.1 to
 2. 